high temperature resistant paint

high temperature resistant paint:Introduction:
HW61-160 Salt, acid, alkali and high temperature resistant paint made of two different parts (A,B). This made from epoxy resin, modified resin, inorganic scales filling, activity agent, additives, etc. The product is a long lasting anticorrosion paint, as well as high adhesive strength, tight structure, high impact resistant properties, seawater resistant, pulverization of salt resistant, chemical air resistant, etc.
high temperature resistant paint:Technical indicators:
Physical Properties

Items	Units	Indicators	Experimental Reference
Specific Gravity	/	Red, gray, others	GB1729-79
Color	/	1.4	GB1756-79
Viscosity(25degree)	S	80-140	GB1751-88
Drying time(25degree)	h	Surface≤3, Hardl≥24	GB1728-88
Solid Content	%	≥75	GB1725-79
Adhesion	Class	1	GB1720-79
Impact Strength	Kg·cm	50	GB1732-79
Flexibility	mm	1	GB1731-79
Wearability(1kg, 500turns weightlessness)	g	<0.05	GB1768-79

Chemical Resistance Properties

Items	Units	Indicators	Experimental Reference
H2SO4 (25%,250)	day	60,No foam, No scale, slight fading	GB1763-79
HNO3 (12%,250)	day	60,No foam, No scale, slight fading	GB1763-79
HCL(10%,250)	day	60,No foam, No scale, slight fading	GB1763-79
NaOH(25%,250)	day	60,No foam, No scale, slight fading	GB1763-79
SALT(5%,250)	day	180No foam, No scale, slight fading	GB1763-79
Petrol (250)	day	18,No foam, No scale, slight fading	GB1734-79
Pulverization of salt	hour	1000,No foam, No scale, slight fading	GB1771-79
Comprehensive Assessment	/	Good	GB1766-79

Application: It is use on the surface of road tube, oil tank, as well as steel and concrete.
Specifications:
Color: red, black (primer), gray, green
Specific Gravity: 1.4
Dosage: 0.3kg/m2
The Thickness: 125um (wet)
The Thickness: 80um (dry)
Ratio: 100:10 (A:B)
Application Time: 4hours, 25degree
Application Methods: bush, roll, spray
Diluents: special <8%
Surface Dry: 1hour, 25degree
Hard Dry: 24hours, 25degree
Solidify: 7 days
The Interval between two washing: 24 hours (shortest time), 100c
7days (longest time), 10degree
8 hours (shortest time), 25degree
3days (longest time), 25degree
6 hours (shortest time), 35degree
4days (longest time), 35degree

Surface Finish: The surface of steel should meet the Swedish 2.5 or St3 standard
Duration period: 12 months
Flash Point: 20degree